A convenient method of preparing ultrafine polystyrene latex nano-particles with chlorine groups on the surface is developed. Polystyrene latexes in the size range 50–400 nm were prepared via emulsion polymerization, using sodium dodecyl sulfate (SDS) as surfactant. The poly styrene with chlorine groups on the surface will be fine to use as organic filler to modify rubber. Transmission electron microscopy (TEM) was used to observe the morphology of silicon dioxide and functionalized polystyrene nanoparticles. The nature of bonding between the polymer and the reactive groups on the filler surfaces was analyzed using Fourier transform infrared spectroscopy (FTIR). Scanning electron microscopy (SEM) was employed to examine the filler surface.

This study investigate the removal efficiency of chromium (VI) from water by using (R-AgCl) Silver chloride resin (SCR) as selective sorbent material for removal chromium (VI) from aqueous solution; the study was carried out by sorption batch experiments at room temperature(25°C). Efficiency of Cr(VI) removal was determined by measuring the chromium concentration before and after the sorption process. Atomic absorption spectroscopy (AAS) method has been applied as analytical method for determination of Cr concentration in water. Governing factors for removal efficiency were proposed, analyzed and compared. It was conducted that the process is mostly affected by pH value of solution, mass of sorbent and concentration of Cr(VI) , which was the most efficient sorbent showed maximal efficiency and maximal sorption capacity, 1.5g of SCR after 60 min at 25 °C and pH 6.5 recovered 98% of Cr(VI) from 100 mL of water polluted with 20 mg of Cr(VI).

A convenient method of preparing ultrafine polystyrene latex nano-particles with amino groups on the surface is developed. polystyrene latexes in the size range 50–400 nm were prepared via emulsion polymerization, using sodium dodecyl sulfate (SDS) as surfactant. The poly styrene with amino groups on the surface will be fine to use as organic filler to modify rubber. Transmission electron microscopy (TEM) was used to observe the morphology of silicon dioxide and functionalized polystyrene nanoparticles. The nature of bonding between the polymer and the reactive groups on the filler surfaces was analyzed using Fourier transform infrared spectroscopy (FTIR). Scanning electron microscopy (SEM) was employed to examine the filler surface.  

Luotonins and its derivatives (Isoluotonins) are alkaloids from the aerial parts of Peganum nigellastrum Bunge. that display three major skeleton types. Luotonins A, B, and E are pyrroloquinazolinoquinoline alkaloids,. A few methods were known for the sysnthesis of Isoluotonin All luotonins have shown promising cytotoxicities towards selected human cancer cell lines, especially against leukemia P-388 cells. Luotonin A is the most active one, with its activity stemming from topoisomerase I-dependent DNAcleavage. Such intriguing biological activities and unique structures have led not only to the development of synthetic methods for the efficient synthesis of these compounds, but also to interest in structural modifications for improving the biological properties. Recent progress in the study of luotonins is covered. 

Brominated butyl rubber (BIIR) was crosslinked through an esterification reaction using the sodium salt of dicyclopentadiene dicarboxylic acid (DCPDCA) as crosslinking agent. The crosslinked BIIR could de-crosslink upon heating and re-crosslink upon cooling due to Diels-Alder type reversible de-dimerization/re-dimerization of dicyclopentadiene moieties in the rubber networks. Torque measurement of the crosslinked rubber was conducted at various temperatures using a typical curemeter to investigate the thermo-reversibility. It was revealed that proper temperature for thermal processing of the crosslinked BIIR would be around 174 °C, at which the crosslinked polymer exhibits good flowability and is not too high to induce unexpected side reactions. The torque measurement was also carried out to investigate the efficiency of antioxidant on retarding the loss of the thermo-reversibility of the crosslinked polymer during heating-cooling cycles. It was found that addition of antioxidant 2246 [2,2′-methylenebis(6-tert-butyl-4-methylphenol)] into BIIR could significantly improve the thermo-reversibility of DCPDCA crosslinked BIIR. Torque measurement provides a convenient and sensitive method to understand the thermal behavior of reversible covalent crosslinked polymer.